Passive nitrogen oxide adsorber catalyst

ABSTRACT

The present invention relates to a catalyst comprising a carrier substrate of the length L, a passive nitrogen oxide adsorber and means to control the temperature of the carrier substrate, as well as a process for cleaning of an exhaust gas emitted from a lean burn engine.

The present invention relates to a catalyst which comprises a passivenitrogen oxide adsorber (PNA) coated on a substrate that enables activetemperature management of the catalyst.

The exhaust gas of motor vehicles that are operated with lean-burncombustion engines, such as diesel engines, also contain, in addition tocarbon monoxide (CO) and nitrogen oxides (NOx), components that resultfrom the incomplete combustion of the fuel in the combustion chamber ofthe cylinder. In addition to residual hydrocarbons (HC), which areusually also predominantly present in gaseous form, these includeparticle emissions, also referred to as “diesel soot” or “sootparticles.” These are complex agglomerates from predominantlycarbonaceous particulate matter and an adhering liquid phase, whichusually preponderantly consists of longer-chained hydrocarboncondensates. The liquid phase adhering to the solid components is alsoreferred to as “Soluble Organic Fraction SOF” or “Volatile OrganicFraction VOF.”

To clean these exhaust gases, the aforementioned components must beconverted to harmless compounds as completely as possible. This is onlypossible with the use of suitable catalysts.

A known method for the removal of nitrogen oxides contained in exhaustgas in the presence of oxygen is the selective catalytic reduction withammonia in the presence of an SCR catalyst. This method comprisesconversion of nitrogen oxides to be removed from the exhaust gas withammonia as reductant into nitrogen and water.

Suitable SCR catalysts are for example zeolites which are ion-exchangedwith iron and in particular with copper, see for example WO2008/106519A1, WO2008/118434 A1 and WO2008/132452 A2.

SCR catalysts for the conversion of nitrogen oxides with ammonia do notcomprise noble metals, in particular no platinum. This is because in thepresence of these metals the oxidation of ammonia with oxygen tonitrogen oxides would be preferred and the SCR reaction (conversion ofammonia with nitrogen oxide) would fall behind. In literature, someauthors speak from platinum-exchanged “SCR catalysts”. However, thisdoesn't refer to the NH₃-SCR-reaction but to the reduction of nitrogenoxides with hydrocarbons. As the selectivity of the latter reaction isvery limited, it would be more correct to call it “HC-DeNOx-reaction”instead of “SCR reaction”.

The ammonia used in the SCR reaction can be made available via feedingof an ammonia precursor, such as urea, ammonium carbamate or ammoniumformate, into the exhaust gas line and subsequent hydrolysis.

SCR catalyst have the drawback that they are operable as of exhaust gastemperatures of about 180 to 200° C. only. Even if recent publicationsare stating that SCR catalysts can be active at as low as 150° C., it isstill a problem to have them remove nitrogen oxides that are formedduring the cold start period of the engine.

In addition to SCR catalysts, in order to remove nitrogen oxidesso-called nitrogen oxide storage catalysts are known. For thesecatalysts the term “Lean NOx Trap,” or LNT, is common. Their cleaningaction is based upon the fact that in a lean operating phase of theengine, the nitrogen oxides are predominantly stored in the form ofnitrates by the storage material of the storage catalyst, and thenitrates are broken down again in a subsequent rich operating phase ofthe engine, and the nitrogen oxides which are thereby released areconverted with the reducing exhaust gas components in the storagecatalyst to nitrogen, carbon dioxide, and water. This operatingprinciple is described in, for example, SAE document SAE 950809.

As storage materials, oxides, carbonates, or hydroxides of magnesium,calcium, strontium, barium, alkali metals, rare-earth metals, ormixtures thereof come, in particular, into consideration. As a result oftheir alkaline properties, these compounds are able to form nitrateswith the acidic nitrogen oxides of the exhaust gas and to store them inthis way. They are deposited in the most highly dispersed form possibleon suitable substrate materials in order to produce a large interactionsurface with the exhaust gas. In addition, nitrogen oxide storagecatalysts generally contain noble metals such as platinum, palladium,and/or rhodium as catalytically active components. It is their purpose,on the one hand, to oxidize NO to NO₂, as well as CO and HC to CO₂, andH₂O under lean conditions and, on the other hand, to reduce released NO₂to nitrogen during the rich operating phases, in which the nitrogenoxide storage catalyst is regenerated.

Modern nitrogen oxide storage catalysts are for example disclosed inEP0885650 A2, US2009/320457, WO2012/029050 A1 and WO2016/020351 A1.

The method described in SAE document SAE 950809, which comprises storingnitrogen oxides during a lean operating phase and releasing them in asubsequent rich operating phase, is also known as “active” nitrogenoxide storing method.

In addition, a method has been described which is known as “passive”nitrogen oxide storing method. This method comprises storing nitrogenoxides in a first temperature window and releasing them in a secondtemperature window where the second temperature window is at highertemperatures than the first temperature window. For carrying out thismethod passive nitrogen oxide adsorber catalysts are used, which arealso known as PNA (“passive NOx-adsorber”).

By means of passive NO_(x)-adsorbers, it is possible to store nitrogenoxides at temperatures, at which a SCR catalyst has not yet reached itsoperating temperature and to release them as soon as the SCR catalyst isoperative. Accordingly, the intermediate storage of nitrogen oxidesbelow for example 200° C. and their release above 200° C. results in anincreased total conversion of nitrogen oxides of a combination ofpassive NOx-adsorber and SCR catalyst.

It is known from literature to use palladium supported on ceria aspassive nitrogen oxide adsorber catalyst, see for example WO2008/047170A1 and WO2014/184568 A1. According to WO2012/071421 A2 and WO2012/156883A1 palladium on ceria can be coated on a particle filter as well.

WO2012/166868 A1 teaches to use a zeolite which comprises for examplepalladium and an additional metal, like for example iron, as passivenitrogen oxide adsorber catalyst.

WO2015/085303 A1 discloses passive nitrogen oxide adsorber catalysts,which comprise a noble metal and a small pore molecular sieve with amaximum ring size of eight tetrahedral atoms.

Ever tightening emission requirements for nitrogen oxides requiredevelopment of new aftertreatment, engines, and systems controltechnologies. Of the aftertreatment technologies considered, nitrogenoxides adsorber catalysts are of high interest because they enablebetter cold start performance by storing the nitrogen oxides until asecondary aftertreatment device is warm enough to convert the nitrogenoxides catalytically. The concept of a passive nitrogen oxides adsorbercatalyst is gaining widespread attention because it has an advantageover a fully formulated, “active” nitrogen oxide adsorber catalystbecause—as described above—it can be regenerated thermally during normaloperation therefore minimizing any additional fuel penalty.

One of the significant challenges for effective operation of a passivenitrogen oxide adsorber catalyst is to synchronize the nitrogen oxiderelease with the time in which a downstream SCR catalyst is active andin which the temperature of the exhaust is warm enough for the dosedurea to hydrolyze to ammonia.

If release is too soon then nitrogen oxides will slip past the catalystand out of the exhaust. If release is too late then the SCR catalyst maybe overwhelmed with nitrogen oxides and not effectively reduce all ofit, also resulting in nitrogen oxide slip.

In particular, passive nitrogen oxide adsorber technologies that use apalladium containing chabazite zeolite release nitrogen oxides attemperatures in excess of 250° C., due to a relatively strong Pd—NObond. This results in the nitrogen oxide adsorber ending the drive cyclein a “fully loaded” condition and therefore not having capacity fornitrogen oxide storage on a subsequent cold start or cold operatingcondition when the SCR catalyst is no longer active. Hence, any nitrogenoxide created by the engine will slip out to the environment. Similarly,these same passive nitrogen oxide adsorber technologies are alsochallenged with SOx release.

Accordingly, in order to be most effective at managing nitrogen oxides,the passive nitrogen oxide adsorber catalyst should have a high nitrogenoxide trapping efficiency (e.g. 90%), good thermal durability, faststorage response and nitrogen oxide release characteristics that alignwith when the downstream SCR catalyst is active. In addition it shouldhave the ability for desulfation at temperatures that do not result insevere thermal degradation.

It has now been found that the above described technical problems can besolved via an effective way to manage the temperature of the catalyst.

Accordingly, the present invention relates to a catalyst comprising acarrier substrate of the length L, a passive nitrogen oxide adsorber andmeans to control the temperature of the carrier substrate.

In an embodiment of the present invention, the passive nitrogen oxideadsorber comprises palladium which is supported on cerium oxide,zirconium oxide, a mixture of cerium and zirconium oxides or on azeolite.

In case the palladium is supported on a zeolite, the zeolite is inparticular a small pore zeolite belonging to a framework type having theframework type code AEI, AFX, CHA, ERI, KFI or LEV.

Zeolites of the framework type AEI are for example SSZ-39 and AIPO-18. Azeolite of the framework type AFX is for example SAPO-56. Zeolites ofthe framework type CHA are for example SSZ-13, SAPO-34, LZ-218, ZK-14and chabazite. Zeolites of the framework type ERI are for exampleZSM-34, LZ-220 and SAPO-17. A zeolite of the framework type KFI is forexample ZK-5. Zeolites of the framework type LEV are for example Levyne,LZ-132, Nu-3, ZK-20 and SAPO-35.

Alternatively, the palladium can be supported on a zeolite belonging tothe framework type having the framework type code BEA or MFI. Zeolitesof the framework type BEA are in particular known as “zeolite beta” or“β zeolite”. A zeolite of the framework type MFI is ZSM-5.

In case the palladium is supported on a zeolite, the zeolite ispreferably chabazite, SSZ-13, zeolite beta or ZSM-5.

In case the palladium is supported on a zeolite, it is in particularpresent within the zeolite structure as palladium cation, i.e. in ionexchanged form. In addition, the palladium can completely or partly bepresent in form of palladium metal and/or in form of palladium oxidewithin the zeolite structure and/or on the surface of the zeolitestructure.

Besides supporting palladium on a zeolite as described above it is alsopreferred to support it on cerium oxide.

The palladium can be present in an amount of 0.01 to 20 weight percentrelative to the weight of the passive nitrogen oxide adsorber andcalculated as palladium metal.

Preferably, palladium is present in an amount of 0.5 to 10, morepreferably 0.5 to 4 and in particular preferably 0.5 to 2 weight percentrelative to the weight of the passive nitrogen oxide adsorber andcalculated as palladium metal.

In an embodiment of the present invention the carrier substrate of thelength L is made of metal, like for example steel or alloys comprisingiron, aluminum and chrome. However, the substrate of the length L can ofcourse be made of cordierite as well.

Such carrier substrates preferably have a high cell density and acorresponding high catalytically effective surface.

In an embodiment, they are designed as flow through substrate where thechannels which are open at both ends extend between the carrier's twoend faces.

Preferably, carrier substrates made of metal are used which have theso-called LS-design (longitudinal structured), the so-called PE-design(perforated foils) or have a combination of both (LS-/PE-design). Inthese carrier structures the walls of the channels are perforated andthe exhaust gas which entered a certain channel is mixed with exhaustgas which entered another channel. This results in turbulent flowconditions in the channel and thus to an increase of the mass transportto the wall onto which the passive nitrogen oxide adsorber is coated.

In another embodiment the carrier substrate is designed to trap soot.Carrier substrates made of metal are described in literature andavailable on the market.

In an embodiment of the present invention the means to control thetemperature of the carrier substrate is at least one electrical heatingelement comprised of metal or ceramic. Usually, a resistive heatingelement is used but other heating elements can be used as well. Theheating element ideally comprises means to control the rate of heating.

Such heating elements are described in literature and are available onthe market. There are even carrier substrates made of metal availablewhich comprise an integrated heating element. Such products are known asEHC—Electrically Heated Catalyst—(see for example SAE paper SAE 951072)and available on the market.

In an embodiment of the present invention the passive nitrogen oxideadsorber is present as a coating on the carrier substrate. In that casethe coating can extend to the total length L of the carrier substrate oronly to a part of it. In case an electrically heated catalyst (EHC) isused as carrier substrate the passive nitrogen oxide adsorber can evenbe coated directly on the heating element.

Also, the passive nitrogen oxide adsorber can be the sole coating on thecarrier substrate or there can be one or more additional catalyticallyactive coatings.

For example, the carrier substrate can carry an oxidation catalystbesides the passive nitrogen oxide adsorber.

The oxidation catalyst comprises for example platinum, palladium orplatinum and palladium on a carrier material. In the latter case theweight ratio of platinum and palladium is for example 4:1 to 14:1.

As carrier material all materials can be used which are known to theskilled person for that purpose. Usually, they have a BET surface of 30to 250 m²/g, preferably of 100 to 200 m²/g (determined according toGerman standard DIN 66132) and are in particular alumina, silica,magnesia, titania, as well as mixtures or mixed oxides comprising atleast two of these materials.

Preferred are alumina, alumina/silica mixed oxides and magnesia/aluminamixed oxides. In case alumina is used, it is preferably stabilized, forexample with 1 to 6 weight percent, in particular 4 weight percent, oflanthana.

The coating comprising the passive nitrogen oxide adsorber (hereaftercalled coating A) and the coating comprising the oxidation catalyst(hereafter called coating B) can be arranged on the carrier substrate indifferent manner.

For example both coatings can extend to the complete length L of thecarrier substrate or only to a part of it.

In one embodiment coating A extends starting from one end of the carriersubstrate to 10 to 80% of the length L and coating B extends startingfrom the other end of the carrier substrate to 10 to 80% of the length Las well. In this case L=L_(A)+L_(B) can apply, wherein L_(A) is thelength of coating A and L_(B) is the length of coating B. However, it isalso possible that L<L_(A)+L_(B) applies. In this case coatings A and Boverlap. Finally, L>L_(A)+L_(B) can apply, if a part of the carriersubstrate is free of any coating. In the latter case there is a gapbetween coatings A and B, which has a length of at least 0.5 cm, forexample 0.5 to 1 cm.

It is also possible that both coatings A and B can extend to thecomplete length L of the carrier substrate. In this case coating B canbe applied directly onto the carrier substrate and coating A ontocoating B. Alternatively, coating A can be applied directly onto thecarrier substrate and coating B onto coating A.

In addition it is possible that one coating extends to the completelength L of the carrier substrate and the other only to a part of it.

In a preferred embodiment of the present invention the coatingcomprising the passive nitrogen oxide adsorber is applied directly ontothe carrier substrate and a coating comprising an oxidation catalyst isapplied onto that coating, both extending to the complete length L ofthe carrier substrate.

In a particular preferred embodiment of the present invention a firstcoating comprising a zeolite selected from the group consisting ofchabazite, SSZ-13, zeolite beta and ZSM-5 which is ion-exchanged withpalladium in amount of 0.5 to 1.5 weight percent, relative to thepassive nitrogen oxide adsorber and calculated as palladium metal, iscoated onto a carrier substrate made of metal and a second coatingcomprising platinum, palladium or platinum and palladium in a weightratio of 4:1 to 14:1 is applied onto the first coating, wherein bothcoatings extend to the complete length L of the carrier substrate.

In that case the lower layer is in particular present in an amount of 50to 250 g/I carrier substrate and the upper layer in an amount of 50 to100 g/I carrier substrate.

Catalysts according to the present invention wherein a passive nitrogenoxide adsorber is present as a coating on the carrier substrate can bemanufactured by known methods, for example in accordance with thecustomary dip coating methods or pump and suck coating methods withsubsequent thermal post-treatment (calcination and possibly reductionusing forming gas or hydrogen). These methods are sufficiently knownfrom the prior art.

The catalysts according to the present invention are outstandinglysuitable as passive nitrogen oxide adsorbers. That means they are ableto store nitrogen oxides at temperatures below 200° C. and to releasethem at temperatures above 200° C. In addition it is possible to manageits temperature so that it ends a drive cycle in an “empty” conditionand therefore provides its full capacity for nitrogen oxide storage on asubsequent cold start or cold operating condition when the SCR catalystis no longer active. Consequently, it is—in combination with adownstream SCR catalyst—possible to effectively convert nitrogen oxideswithin the complete temperature range, including cold starttemperatures.

Accordingly, the present invention also relates to an exhaust gascleaning system which comprises

-   -   a catalyst comprising a carrier substrate of the length L, a        passive nitrogen oxide adsorber and means to control the        temperature of the carrier substrate, and    -   a first SCR catalyst.

The first SCR catalyst of the inventive exhaust gas cleaning system canprincipally be selected from all catalysts which are active incatalyzing the SCR reaction of nitrogen oxides with ammonia. Inparticular the first SCR catalyst is selected from SCR catalysts beingcustomary in the field of cleaning of automotive exhaust gas. Thatcomprises SCR catalysts of the mixed oxide type, which for examplecomprise vanadium, tungsten and titanium, as well as catalysts on thebasis of zeolites, in particular zeolites which are exchanged withtransition metals, in particular with copper, iron or iron and copper.

In embodiments of the present invention the first SCR catalyst comprisessmall pore zeolites with a maximum ring size of eight tetrahedral atomsand a transition metal, for example copper, iron or copper and iron.Such SCR catalysts are for example disclosed in WO2008/106519 A1,WO2008/118434 A1 and WO2008/132452 A2.

In addition, large and medium pore sized zeolites which are exchangedwith transition metals can be used as well. Of interest are inparticular zeolites belonging to the structure code BEA.

In particular preferred zeolites belong to the structure codes BEA, AEI,CHA, KFI, ERI, LEV, MER or DDR and are in particular ion-exchanged withcopper, iron or copper and iron.

Within the context of the present invention the term zeolites comprisesmolecular sieves which are sometimes called “zeolite-like”. Molecularsieves are preferred if they belong to one of the above mentionedstructure codes. Examples are silicaaluminumphosphate-zeolites, whichare known as SAPO and aluminumphosphate-zeolites, which are known asAIPO. As well, these materials are in particular preferred if they areexchanged with copper, iron or iron and copper.

In addition, preferred zeolites have a SAR (silica-to-alumina ratio)value of 2 to 100, in particular 5 to 50.

The zeolites and molecular sieves, respectively, comprise transitionmetal in particular in an amount of 1 to 10 weight percent, preferred 2to 5 weight percent, calculated as metal oxide, like for example Fe₂O₃or CuO.

In preferred embodiments of the present exhaust gas cleaning system thefirst SCR catalyst comprises zeolites or molecular sieves of theBeta-type (BEA), Chabazite-type (CHA) or Levyne-type (LEV). Suchzeolites or molecular sieves are for example known as ZSM-5, Beta,SSZ-13, SSZ-62, Nu-3, ZK-20, LZ-132, SAPO-34, SAPO-35, AIPO-34 andAIPO-35, see for example U.S. Pat. Nos. 6,709,644 and 8,617,474.

In an embodiment of the inventive exhaust gas cleaning system there is adosing unit for reductant between the catalyst comprising a passivenitrogen oxide adsorber and the first SCR catalyst.

Suitable dosing units can be found in literature (see for example T.Mayer, Feststoff-SCR-System auf Basis von Ammonium-carbamat,Dissertation, Technical University of Kaiserslautern, Germany, 2005) andthe skilled person can select any of them. The ammonia can be dosed intothe exhaust gas flow as such or in form of a precursor which formsammonia at the ambient conditions of the exhaust gas flow. Suitableprecursors are for example aqueous solutions of urea or ammonium format,as well as solid ammonium carbamate. The reductant and its precursor,respectively, is usually carried in a storage tank which is connected tothe dosing unit.

The first SCR catalyst is usually present in form of a coating on acarrier substrate, which may be a flow through or a wall flow substrate.The carrier substrate consists of for example silicon carbide, aluminumtitanate or cordierite.

The inventive exhaust gas cleaning system optionally contains additionalelements. For example, it can comprise a second SCR catalyst which canbe located downstream of the first SCR catalyst or which can be locatedupstream of the catalyst comprising a passive nitrogen oxide adsorber ina closed-coupled position. The second SCR catalyst preferably compriseszeolites which are disclosed as being preferred for the first SCRcatalyst above.

In addition, the inventive exhaust gas cleaning system can comprise aso-called ammonia slip catalyst (ASC). The purpose of an ammonia slipcatalyst is to oxidize ammonia which breaks through an SCR catalyst andthus to avoid its release to atmosphere. Consequently, an ammonia slipcatalyst is coated on a separate carrier substrate and locateddownstream of an SCR catalyst or it is coated on a downstream part of anSCR catalyst. In embodiments of the inventive exhaust gas cleaningsystem the ammonia slip catalyst comprises one or more platinum groupmetals, in particular platinum or platinum and palladium.

The inventive catalyst allows to align its nitrogen oxide releasecharacteristics with when the downstream SCR catalyst is active.

Accordingly, the present invention relates to a process for cleaningexhaust gas emitted from a lean burn engine and containing nitrogenoxides, which process comprises contacting the exhaust gas stream withan exhaust gas cleaning system comprising

-   -   a catalyst comprising a carrier substrate of the length L, a        passive nitrogen oxide adsorber and means to control the        temperature of the carrier substrate, and    -   a first SCR catalyst

thereby

a) storing nitrogen oxides in the passive nitrogen oxide adsorber attemperatures lower than the operating temperature range of the first SCRcatalyst

b) releasing nitrogen oxides stored in step a) as soon as the first SCRcatalyst has reached its operating temperature range by heating thecarrier substrate and

c) reducing the nitrogen oxides released in step b) in the first SCRcatalyst.

EXAMPLE 1

a) A zeolite of the type SSZ-13 (framework type code CHA) is impregnatedwith 2% by weight of palladium using commercially available palladiumnitrate (“incipient wetness”). The powder obtained is subsequently driedstepwise at 120 and 350° C. and finally calcined at 500° C.

b) The Pd-containing powder obtained in step a) above is suspended indemineralised water, mixed with 8% of a commercially available binderbased on boehmite and milled in a ball mill. Subsequently, the washcoatobtained is coated on an electrically heated catalyst (EHC) made ofmetal (commercially available for example with the tradename EMICAT®)over its total length. The washcoat loading is 50 g/L, relative to thePd-containing zeolite. This corresponds with a Pd-loading of 42.5 g/ft³.

EXAMPLE 2

Example 1 is repeated with the difference that a zeolite of theframework typ BEA is used.

EXAMPLE 3

The catalyst obtained according to Example 1 is in an additional stepcoated over its total length with a washcoat comprising platinumsupported on alumina. The washcoat loading of the additional step is 75g/L, the platinum loading is 20 g/ft.

EXAMPLE 4

The catalyst obtained in Example 3 is combined with a second catalyst toform an exhaust gas cleaning system. The second catalyst is acommercially available flow through substrate made of cordierite whichcarries a zeolite of the framework typ CHA which is ion-exchanged with3% by weight of copper (calculated as CuO). The washcoat loading of thesecond catalyst is 150 g/L.

The invention claimed is:
 1. A catalyst comprising: a carrier substrateof length L, passive nitrogen oxide adsorber material supported on thecarrier substrate; and a heating member that is positioned to heat thepassive nitrogen oxide adsorber material at a time when exhaust flowsover the passive nitrogen oxide adsorber material, wherein the heatingmember is a heating element supported on or integrated with the carriersubstrate, and the passive nitrogen oxide adsorber material is a layerof passive nitrogen oxide adsorber material supported by the carriersubstrate, and wherein the passive nitrogen oxide adsorber material iscoated such that that the exhaust flow that is heated by the heatingmember travels over the passive nitrogen oxide adsorber material. 2.Catalyst according to claim 1, wherein the passive nitrogen oxideadsorber comprises palladium which is supported on cerium oxide,zirconium oxide, a mixture of cerium and zirconium oxides or on azeolite.
 3. Catalyst according to claim 2, wherein the palladium issupported on a zeolite and the zeolite is a small pore zeolite belongingto a framework type having the framework type code AEI, AFX, CHA, ERI,KFI or LEV or belongs to the framework type code BEA or MFI.
 4. Catalystaccording to claim 2, wherein palladium is supported on cerium oxide. 5.Catalyst according to claim 2, wherein palladium is present in an amountof 0.01 to 20 weight percent relative to the weight of the passivenitrogen oxide adsorber and calculated as palladium metal.
 6. Catalystaccording to claim 1, wherein the heating element is a resistive heatingelement.
 7. Catalyst according to claim 1, wherein the carrier substrateof the length L is made of metal.
 8. Catalyst according to claim 1,wherein the carrier substrate of the length L is an electrically heatedcatalyst (EHC).
 9. Catalyst according to claim 8, wherein the passivenitrogen oxide adsorber is present as a coating over the full length ofthe carrier substrate of the length L.
 10. Catalyst according to claim9, wherein the carrier substrate of the length L comprises one or morecatalytically active coatings besides the passive nitrogen oxideadsorber.
 11. Catalyst according to claim 10, wherein the carriersubstrate of the length L comprises an oxidation catalyst besides thepassive nitrogen oxide adsorber.
 12. Exhaust gas cleaning system whichcomprises the catalyst of claim 1, and a first SCR catalyst.
 13. Exhaustgas cleaning system according to claim 12, wherein the first SCRcatalyst comprises a small pore zeolite with a maximum ring size ofeight tetrahedral atoms and a transition metal.
 14. The exhaust gascleaning system according to claim 13, wherein the transition metal iscopper, iron or copper and iron.
 15. Exhaust gas cleaning systemaccording to claim 12, wherein the first SCR catalyst comprises azeolite belonging to the structure code BEA, AEI, CHA, KFI, ERI, LEV,MER or DDR and which is ion-exchanged with copper, iron or copper andiron.
 16. Exhaust gas cleaning system according to claim 12, whichcomprises a dosing unit for reductant between the catalyst comprising apassive nitrogen oxide adsorber and the first SCR catalyst.
 17. Exhaustgas cleaning system according to claim 12, which comprises a second SCRcatalyst which is located downstream of the first SCR catalyst or islocated upstream of the catalyst comprising a passive nitrogen oxideadsorber in a closed-coupled position.
 18. Exhaust gas cleaning systemaccording to claim 12, which comprises an ammonia slip catalyst. 19.Process for cleaning of an exhaust gas emitted from a lean burn engineand containing nitrogen oxides, which process comprises contacting theexhaust gas stream with the exhaust gas cleaning system of claim
 12. 20.The exhaust gas cleaning system according to claim 1, wherein thepassive nitrogen oxide adsorber material is coated as to extend over adownstream side of the carrier support being heated.
 21. A catalystcomprising: a carrier substrate of length L, passive nitrogen oxideadsorber material supported on the carrier substrate; and a heatingmember that is positioned to heat the passive nitrogen oxide adsorbermaterial at a time when exhaust flows Over the passive nitrogen oxideadsorber material, wherein the heating member is a heating elementsupported on or integrated with the carrier substrate, and the passivenitrogen oxide adsorber material is a layer of passive nitrogen oxideadsorber material supported by the carrier substrate, and wherein thepassive nitrogen oxide adsorber material is coated as to extend over adownstream side of the carrier support being heated wherein the heatingmember is an electrically heated substrate of metal material and thepassive nitrogen oxide adsorber material, which includes Pd-containingzeolite, is coated directly on the electrically heated substrate ofmetal material and over the full length of the heating member. 22.Catalyst according to claim 11, wherein the oxidation catalyst isapplied over the passive nitrogen oxide adsorber material over the fulllength of L, and wherein the passive nitrogen oxide adsorber materialincludes Pd-containing zeolite and the oxidation catalyst comprisesplatinum.
 23. A catalyst comprising: a carrier substrate of axial lengthL, passive nitrogen oxide adsorber material supported on the carriersubstrate; and a heating member that is positioned to heat the passivenitrogen oxide adsorber material at a time when exhaust flows over thepassive nitrogen oxide adsorber material, wherein the heating member isa heating element integrated with the carrier substrate as to be locatedaxially within length L of the carrier Substrate, and the passivenitrogen oxide adsorber material is a layer of passive nitrogen oxideadsorber material supported by the carrier substrate, and wherein thepassive nitrogen oxide adsorber material is coated as to axially overlapthe heating element as to provide for temperature control of the passivenitrogen oxide adsorber material at a time when exhaust flows over thepassive nitrogen oxide adsorber material.